6063 Aluminium Pipe

6063 aluminum rod (Aluminum 6063 T5 Cylinder Tube Supplier) is a low-alloy Al-Mg-Si series high plastic alloy. Has many valuable features: 1. Heat treatment strengthened, high impact toughness, insensitive to defects. 2. It has excellent thermoplasticity and can be extruded at high speed into complex, thin-walled, hollow profiles or forgings with complex structures. The quenching temperature range is wide, and the quenching sensitivity is low. After extrusion and forging demoulding, As long as the temperature is higher than the quenching temperature. It can be quenched by spraying or penetrating water. Thin-walled parts (6<3mm) can also be wind quenched. 3. Excellent welding performance and corrosion resistance, no stress corrosion cracking tendency. Among the heat-treatable aluminum alloys, the Al-Mg-Si series alloy is the only alloy that has no stress corrosion cracking phenomenon. 4. After processing, the surface is very smooth and easy to anodize and color. The disadvantage is that after quenching, if it is left at room temperature for a period of time and then aging, it will have an adverse effect on the strength (parking effect).

6063 Aluminum Bar is a medium-strength heat-treatable and strengthened alloy in the AL-Mg-Si series. Mg and Si are the main alloying elements. The main task of optimizing the chemical composition is to determine the percentage of Mg and Si (mass fraction, the same below) .

1.1 The role and influence of Mg Mg and Si form the strengthening phase Mg2Si. The higher the content of Mg, the more the amount of Mg2Si, the greater the heat treatment strengthening effect, and the higher the tensile strength of the profile, but the deformation resistance will also increase. Large, the plasticity of the alloy decreases, the processing performance deteriorates, and the corrosion resistance deteriorates.

1.2 The role of Si and the amount of Si should be such that all Mg in the alloy can exist in the form of Mg2Si phase to ensure that the role of Mg is fully exerted. As the Si content increases, the alloy grains become finer, the metal fluidity increases, the casting performance becomes better, the heat treatment strengthening effect increases, the tensile strength of the profile increases, the plasticity decreases, and the corrosion resistance deteriorates.We can offer the 6063 pneumatic cylinder tube for you.

Techincal:

Tensile strength σb (MPa): 130~230

The ultimate tensile strength of 6063 is 124 MPa

Tensile yield strength 55.2 MPa

Elongation rate 25.0%

Elasticity coefficient 68.9 GPa

Bending ultimate strength 228 MPa Bearing Yield Strength 103 MPa

Poisson’s ratio 0.330

Fatigue strength 62.1 MPa

The solution temperature is: 520℃

The annealing temperature is: 415℃×(2-3)h, cooling from 415℃ to 260℃ at a rate of 28℃/h.

Melting temperature: 615~655℃.

Specific heat capacity: 900

Heat treatment process:

Excellent craftsmanship

 

In our workshop, we are 6063 Cylinder Tube (Aluminium 6063 Pipe) Manufacturer and produce Aluminum 6063 T5 Cylinder Tube(China Aluminum Cylinder Barrel).